    Rights statement: This is the author’s version of a work that was accepted for publication in Journal of Alloys and Compounds. Changes resulting from the publishing process, such as peer review, editing, corrections, structural formatting, and other quality control mechanisms may not be reflected in this document. Changes may have been made to this work since it was submitted for publication. A definitive version was subsequently published in Journal of Alloys and Compounds, 854, 2021 DOI: 10.1016/j.jallcom.2020.157250

    Accepted author manuscript, 0.99 MB, PDF document

    Available under license: CC BY-NC-ND

Links

Text available via DOI:

View graph of relations

Microstructural and electrochemical properties of impregnated La0.4Sr0.6Ti0.8Mn0.2O3±d into a partially removed Ni SOFC anode substrate

Research output: Contribution to Journal/MagazineJournal articlepeer-review

Published
  • S.H. Woo
  • S.-W. Baek
  • D.S. Park
  • K.E. Song
  • H. Schlegl
  • J.-Y. Park
  • J.H. Kim
Close
<mark>Journal publication date</mark>15/02/2021
<mark>Journal</mark>Journal of Alloys and Compounds
Volume854
Publication StatusPublished
Early online date22/09/20
<mark>Original language</mark>English

Abstract

The microstructural and electrochemical properties of anodes obtained by impregnation of the La0.4Sr0.6Ti0.8Mn0.2O3±d (LSTM) oxide system into two types of anode substrates such as Ni/ 8YSZ substrate (Ni (E)/ 8YSZ) and partially Ni removed Ni/ 8YSZ substrate (Ni(R)/8YSZ) were investigated in order to apply them as anode material for solid oxide fuel cells. All of the samples with LSTM impregnated on Ni (R)/ 8YSZ show higher electrical conductivity values than those of unimpregnated Ni (E)/ 8YSZ under dry H2 condition. The highest electrical conductivity values of 2041.2, 1877.4, and 1764.3 S/cm at 700, 800 and 900 °C can be achieved by samples with 3 wt% impregnated LSTM on Ni (R)/ 8YSZ. From the XPS analysis, the existence of a Ti metal peak on the surface of LSTM was only measured for the LSTM (3 wt%)-Ni (R)/ 8YSZ sample, metallic titanium on the surface can improve the electrical catalytic reaction. LSTM (3 wt%)-Ni (R)/ 8YSZ showed higher electrical conductivity values then those of LSTM (3 wt%)-Ni (E)/ 8YSZ in all the temperature ranges measured in the case of dry CH4 supply. Finally, the electrical conductivity of LSTM (3 wt%)-Ni (R)/ 8YSZ was stably maintained even when exposed to dry CH4 condition at 900 °C for a long time (100 h). © 2020 Elsevier B.V.

Bibliographic note

This is the author’s version of a work that was accepted for publication in Journal of Alloys and Compounds. Changes resulting from the publishing process, such as peer review, editing, corrections, structural formatting, and other quality control mechanisms may not be reflected in this document. Changes may have been made to this work since it was submitted for publication. A definitive version was subsequently published in Journal of Alloys and Compounds, 854, 2021 DOI: 10.1016/j.jallcom.2020.157250