Degradation of QPPO-based anion polymer electrolyte membrane at neutral pH

Research output: Contribution to Journal/MagazineJournal articlepeer-review

Published
Close
<mark>Journal publication date</mark>5/07/2023
<mark>Journal</mark>RSC Advances
Issue number29
Volume13
Number of pages8
Pages (from-to)20235-20242
Publication StatusPublished
<mark>Original language</mark>English

Abstract

The chemical stability of anion polymer electrolyte membranes (AEMs) determines the durability of an AEM water electrolyzer (AEMWE). The alkaline stability of AEMs has been widely investigated in the literature. However, the degradation of AEM at neutral pH closer to the practical AEMWE operating condition is neglected, and the degradation mechanism remains unclear. This paper investigated the stability of quaternized poly( -phenylene oxide) (QPPO)-based AEMs under different conditions, including Fenton solution, H O solution and DI water. The pristine PPO and chloromethylated PPO (ClPPO) showed good chemical stability in the Fenton solution, and only limited weight loss was observed, 2.8% and 1.6%, respectively. QPPO suffered a high mass loss (29%). Besides, QPPO with higher IEC showed a higher mass loss. QPPO-1 (1.7 mmol g ) lost nearly twice as much mass as QPPO-2 (1.3 mmol g ). A strong correlation between the degradation rate of IEC and H O concentration was obtained, which implied that the reaction order is above 1. A long-term oxidative stability test at pH neutral condition was also conducted by immersing the membrane in DI at 60 °C water for 10 months. The membrane breaks into pieces after the degradation test. The possible degradation mechanism is that oxygen or OH˙ radicals attack the methyl group on the rearranged ylide, forming aldehyde or carboxyl attached to the CH group. [Abstract copyright: This journal is © The Royal Society of Chemistry.]