T1 - Effect of grain size on mechanical characteristics and work-hardening behavior of fine-grained Mg-0.8Mn alloy via adjusting extrusion temperature
AU - Li, C.C.
AU - Qiao, X.G.
AU - Sun, W.T.
AU - Golovin, I.S.
AU - Kim, H.S.
AU - Sakai, T.
AU - Zheng, M.Y.
PY - 2025/1/5
Y1 - 2025/1/5
N2 - In this study, the Mg-0.8Mn (M08, wt%) alloy is subjected to hot extrusion at various temperatures ranging from 150 ℃ to 300 ℃, and the correlations between the microstructure evolution, tensile properties, and work hardening behavior at ambient temperature are elaborated. The M08 alloy extruded at 150 ℃ exhibits a bimodal microstructure, which included undynamic recrystallized (unDRXed) grains and fine dynamic recrystallized (DRXed) grains with an average size of 1.4 μm. As the extrusion temperature exceeds 210 °C, fully DRXed grains can be observed with grains growth becoming more pronounced with the increase of extrusion temperature. Notably, Mn atomic segregations are evident at the grain boundaries (GBs) in the M08 alloy extruded at 150 °C. It is also essential to highlight that the propensity for GB segregation is diminished with higher extrusion temperature, and the amount of α-Mn precipitates within grain interiors is increased in the M08 sample extruded at 300 ℃. An intriguing observation is the abnormal rise in yield strength (YS) with grain size as the extrusion temperature is increased. This phenomenon can be attributed to the diminishing effect of GB sliding and the concurrent enhancement of GB strengthening effect. However, as the extrusion temperature is raised from 150 °C to 300 °C, the ductility of M08 alloy experiences a substantial decline from 74 % ± 4–16 % ± 3 %. Meanwhile, the grain growth can bring about an increased strain hardening rate, which is primarily dependent on the transition in the dominant deformation mechanism from grain boundary sliding (GBS) to dislocation slip. This transition leads to a more substantial accumulation of dislocations within the coarser grains, thereby affecting the mechanical behavior of M08 alloy. This work provides valuable insights into the influence of extrusion temperature on the microstructure evolution and mechanical properties of Mg-0.8Mn alloy, offering a foundation for optimizing the processing parameters to achieve desired mechanical performance.
AB - In this study, the Mg-0.8Mn (M08, wt%) alloy is subjected to hot extrusion at various temperatures ranging from 150 ℃ to 300 ℃, and the correlations between the microstructure evolution, tensile properties, and work hardening behavior at ambient temperature are elaborated. The M08 alloy extruded at 150 ℃ exhibits a bimodal microstructure, which included undynamic recrystallized (unDRXed) grains and fine dynamic recrystallized (DRXed) grains with an average size of 1.4 μm. As the extrusion temperature exceeds 210 °C, fully DRXed grains can be observed with grains growth becoming more pronounced with the increase of extrusion temperature. Notably, Mn atomic segregations are evident at the grain boundaries (GBs) in the M08 alloy extruded at 150 °C. It is also essential to highlight that the propensity for GB segregation is diminished with higher extrusion temperature, and the amount of α-Mn precipitates within grain interiors is increased in the M08 sample extruded at 300 ℃. An intriguing observation is the abnormal rise in yield strength (YS) with grain size as the extrusion temperature is increased. This phenomenon can be attributed to the diminishing effect of GB sliding and the concurrent enhancement of GB strengthening effect. However, as the extrusion temperature is raised from 150 °C to 300 °C, the ductility of M08 alloy experiences a substantial decline from 74 % ± 4–16 % ± 3 %. Meanwhile, the grain growth can bring about an increased strain hardening rate, which is primarily dependent on the transition in the dominant deformation mechanism from grain boundary sliding (GBS) to dislocation slip. This transition leads to a more substantial accumulation of dislocations within the coarser grains, thereby affecting the mechanical behavior of M08 alloy. This work provides valuable insights into the influence of extrusion temperature on the microstructure evolution and mechanical properties of Mg-0.8Mn alloy, offering a foundation for optimizing the processing parameters to achieve desired mechanical performance.
U2 - 10.1016/j.jallcom.2024.177322
DO - 10.1016/j.jallcom.2024.177322
M3 - Journal article
VL - 1010
JO - Journal of Alloys and Compounds
JF - Journal of Alloys and Compounds
SN - 0925-8388
M1 - 177322
ER -