TY - JOUR
T1 - A High-Performance Cr2O3/CaCO3 Nanocomposite Catalyst for Rapid Hydrogen Generation from NaBH4
AU - Alshammari, Majed
AU - Alshammari, Khulaif
AU - Alhassan, Sultan
AU - Alshammari, Alhulw H.
AU - Alotaibi, Turki
AU - Alotibi, Satam
AU - Ismael, Ali
AU - Taha, Taha Abdel Mohaymen
PY - 2024/2/8
Y1 - 2024/2/8
N2 - This study aims to prepare new nanocomposites consisting of Cr2O3/CaCO3 as a catalyst for improved hydrogen production from NaBH4 methanolysis. The new nanocomposite possesses nanoparticles with the compositional formula Cr2−xCaxO3 (x = 0, 0.3, and 0.6). These samples were prepared using the sol-gel method, which comprises gelatin fuel. The structure of the new composites was studied using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, environmental scanning electron microscopy (ESEM), and X-ray spectroscopy (XPS). The XRD data showed the rhombohedral crystallinity of the studied samples, and the average crystal size was 25 nm. The FTIR measurements represented the absorption bands of Cr2O3 and CaO. The ESEM micrographs of the Cr2O3 showed the spherical shape of the Cr2O3 nanoparticles. The XPS measurements proved the desired oxidation states of the Cr2−xCaxO3 nanoparticles. The optical band gap of Cr2O3 is 3.0 eV, and calcium doping causes a reduction to 2.5 and 1.3 eV at 15.0 and 30.0% doping ratios. The methanolysis of NaBH4 involved accelerated H2 production when using Cr2−xCaxO3 as a catalyst. Furthermore, the Cr1.7Ca0.3O3 catalyst had the highest hydrogen generation rate, with a value of 12,750 mL/g/min.
AB - This study aims to prepare new nanocomposites consisting of Cr2O3/CaCO3 as a catalyst for improved hydrogen production from NaBH4 methanolysis. The new nanocomposite possesses nanoparticles with the compositional formula Cr2−xCaxO3 (x = 0, 0.3, and 0.6). These samples were prepared using the sol-gel method, which comprises gelatin fuel. The structure of the new composites was studied using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, environmental scanning electron microscopy (ESEM), and X-ray spectroscopy (XPS). The XRD data showed the rhombohedral crystallinity of the studied samples, and the average crystal size was 25 nm. The FTIR measurements represented the absorption bands of Cr2O3 and CaO. The ESEM micrographs of the Cr2O3 showed the spherical shape of the Cr2O3 nanoparticles. The XPS measurements proved the desired oxidation states of the Cr2−xCaxO3 nanoparticles. The optical band gap of Cr2O3 is 3.0 eV, and calcium doping causes a reduction to 2.5 and 1.3 eV at 15.0 and 30.0% doping ratios. The methanolysis of NaBH4 involved accelerated H2 production when using Cr2−xCaxO3 as a catalyst. Furthermore, the Cr1.7Ca0.3O3 catalyst had the highest hydrogen generation rate, with a value of 12,750 mL/g/min.
KW - General Materials Science
KW - General Chemical Engineering
U2 - 10.3390/nano14040333
DO - 10.3390/nano14040333
M3 - Journal article
VL - 14
JO - Nanomaterials
JF - Nanomaterials
SN - 2079-4991
IS - 4
M1 - 333
ER -